Technical data for X12Cr13 cold-drawn steel wire, compliant with EN 10263-5. View the chemical composition, mechanical properties, and related technical requirements for this grade.
Only data directly related to this material is shown here. Inspection, equipment, process and packaging information is linked separately.
1. Combinations of delivery conditions
Table 1 - Combinations of common heat treatment conditions, product forms, and related requirements
Heat treatment condition upon delivery
Symbol
Product form A
Steels
Applicable requirements
Bar
Rolled wire
Wire
ferritic
martensitic
austenitic and austenitic-ferritic
soft-annealed
+A
X
X
X
X
X
—
Chemical composition according to Table 3
Mechanical properties according to Tables 5 or 6 or 7 or 8
Additional or special requirements according to EN 10263-1 Annex Ab
solution annealed
+AT
X
X
X
—
—
X
Other
Other delivery conditions may be agreed upon at the time of inquiry and order
A X = is applicable – = is not applicable b If agreed upon at the time of inquiry and order
Table 2 – Surface quality under delivery conditions
Surface condition in the delivered condition
Symbol
Bar
Rolled wire
Wire
cold-drawn
+C
X
X
rolled-sheared
+PE
X
X
drawn after rolling, smoothed
+LC
X
2. Chemical composition
Table 3 - Steel grades and chemical composition (cast analysis), mass fraction % a
Table 4 - Limit deviations between product analysis and the limit values for cast analysis given in Table 3
3. Mechanical properties
Table 8 - Mechanical Properties of Martensitic Stainless Steels under Specified Delivery Conditions
steels
locations
Diameter
Delivery condition
+A or +A+PE
+A+LC
+A+C+A
+A+C+A+LC
Abbreviated name
Workpiece material number
Over mm
bis mm
Rm max MPa
Z min %
Rm max MPa
Z min %
Rm max MPa
Z min %
Rm max MPa
Z min %
X12Cr13
1.4006
2
5
600
60
660
58
5
10
600
60
720
57
600
60
640
58
10
25
600
60
700
57
600
60
25
100
600
60
4. Surface
Table 9 - Depth of Surface Defects
Diameter in the delivered condition a mm
Maximum permissible depth of defects b mm
≤10
0,10
>10
1% of the diameter
d For diameters below 5 mm, the permissible depth of surface defects shall be reduced proportionally to the diameter reduction during cold drawing. b For ferritic, martensitic, and austenitic-ferritic steels, higher values may be agreed upon at the time of inquiry and order
TECHNICAL NOTE
Application and ordering note
Chemical composition, mechanical properties, tolerances and delivery condition must be confirmed against the applicable standard edition, customer drawing and order specification.