Technical data for C10E2C cold heading wire, compliant with ISO 4954-Appendix B. View chemical composition, mechanical properties, and related technical requirements for this grade.
Only data directly related to this material is shown here. Inspection, equipment, process and packaging information is linked separately.
1. Combinations of delivery conditions
Table B.1 - Combinations of heat treatment condition at delivery, product form, and applicable requirements
Heat-treatment condition at delivery
Symbol
Products form a
Applicable requirements in cases where the steel concerned has been ordered with reference to the steel names indicated in
Wire rod
Bar
Wire
T a b les B. 2,B.3,B.4 or B.5
Ta bles B. 2,B.3,B.4,B.5,B.6 or B,7
Optional
As hot-rolled or peeled
+AR or +PE
X
X
X
Chemical composition as specified in Table B.2
Mechanical properties as specified in Ta b les B.3, B.4 and B.5
Chemical compositior as specified in Table B.2
Mechanical properties as specified in Tables B.3, B.4 and B.5
Values for hardenability according to Ta b les B.6 and B.7
Supplementa- ry or special requirements as specified in Annex Eh
Cold drawn
+AR+C
-
X
X
Cold drawn + spheroidized
+AR+C+AC
-
X
X
Cold drawn + spheroidized+skin passed
+AR+C+AC +LC
-
X
X
Spheroidized or spheroidized+peeled
+AC or +AC +PE
X
X
X
Spheroidized+cold drawn
+AC+C
X
X
Treated to ferrite- pearlite structure and hardness range
+FP
-
X
-
Others
Other delivery conditions may be agreed at the time of ordering
a X=applicable,-=not applicable. b If agreed at the time of the enquiry and order.
2. Chemical composition
Table B.2 - Chemical composition of steels for surface hardening (applicable to cast analysis)
Steel name b
% mass fraction a
C
Si c
Mn
P
S
Cr
Ni
Mo
B
Cu
C10E2C
0,08 to 0,12
0,30
0,30 to 0,60
0,025
0,025
—
—
0,25
Elements not quoted in this table should not be intentionally added to the steel without the agreement of the purchaser,except those intended for finishing the heat.All reasonable precautions shall be taken in order to prevent the addition of such elements from scrap or other materials used in the production process,which can affect the hardenability, mechanical properties and applicability To improve the performance of cold heading,it is possible to add Al:0,020 %to 0,050 % a Maximum values unless otherwise indicated. b In the case of steels with hardenability requirements (see Tables B.6 and B.Z),minor deviations from the specified limits are permitted (with the exception of sulfur and phosphorus),provided that they do not exceed 0,01 %for carbon and the values indicated in Table 2 for the other elements. c A lower silicon content or a specific silicon range may be agreed at the time of ordering
3. Mechanical properties
Table B.3 - Mechanical properties of non-alloy steel grades
Steel name
Diameter
Delivery condition
+AR or+PE
+AC or+AC+PE
+AR+C
+AR+C+AC
+AR+C+AC+LC
+AC+C
above mm
up to mm
Rm max. MPa
Za min. %
Rm max MPa
Z min. %
Rm max. MPa
Z min. %
Rm max MPa
Z min. %
Rm max. MPa
Z min. %
Rm max. MPa
Z min. %
C10E2C
2
5
—
—
—
—
—
390
67
430
65
—
—
5
10
450
58
400
65
540
56
380
67
420
65
490
62
10
40
450
58
400
65
530
56
380
67
420
65
480
62
40
100
450
58
400
65
—
——
a The values are provided for reference only.
4. Hardenability requirements
TECHNICAL NOTE
Application and ordering note
Chemical composition, mechanical properties, tolerances and delivery condition must be confirmed against the applicable standard edition, customer drawing and order specification.